Payment & Shipping Terms:
|Material:||A3003 Or A5052||Surface:||PVDF Painted|
|Quality Guarantee Period:||15 Years||Size:||1220*2440 Mm2|
|Application:||Shipbuilding||Product Name:||PVDF Painted Aluminum Honeycomb Panel|
honeycomb core board,
honeycomb composite board
PVDF Painted Aluminium Honeycomb Panel with the Edge RHS Sealed for Shipbuilding Industry
PVDF Painted Aluminium Honeycomb Panel with the Edge RHS Sealed for Shipbuilding Industry is the aluminum honeycomb panel with a process of compositing with RHS sealing the Edges, putting sealing gap and PVDF painting the whole panel.
1. It will make the panel with a luxurious but rigid and anti-corrosion surface as a whole panel without any gap on the surfaces.
2. The PVDF painting process is used for the surface treatment of the complicated aluminum honeycomb panels especially the putty filling process is needed. Pasia has experienced a project that should use the PVDF painting process because there are so many gaps and shape edges needed to be filled with putty. Therefore, the panel should be firstly produced into required shapes, then using putty to seal the edge and fill the gap. At last, they were painted in PVDF material to make the panels looked like complete ones.
3. Painting is the practice of applying paint, pigment, color or other medium to a surface (support base).
4. The medium is commonly applied to the base with a brush but other implements, such as knives, sponges, and airbrushes, can be used.
Aluminum honeycomb panel is a bonded sandwich structure system of two surface aluminium plates and one honeycomb cores with a special purpose adhesive. Industrial used aluminium honeycomb panel will add some more processes such as surface treatment, edging, embedding, carving and so on to make the panel suitable for special conditions. It has been widely used by the industries of civil construction, transportation, exhibition, signage, elevator, clean room etc. The honeycomb technology is from aerospace technology. The whole production process is finished in the modern factory, using hot pressing or vacuum pressing technology. Due to the high thermal conductivity between the aluminum plates and honeycomb, it is synchronized the thermal expansion and contraction of the inside and outside aluminium material. There are small holes on the honeycomb core foil wall so that the air is free of flowing inside the panel box. Furthermore, sliding mounting buckle system does not cause structural deformation during thermal expansion and contraction.
The center material is aluminum hexagonal honeycomb with a small density (about 3 to 7 kg per square meter), about 1/5 of the weight of wood with the same area and thickness, 1/6 of the glass, 1/7 of solid aluminium, which greatly reduced the building load and construction cost. Thanks to the air contained in the core, the panel can be sound and thermal insulated. Because of no combustible material contained, the fire rating can be at least B1 level. The panel performs well also on waterproof, moisture-proof, no harmful gas release, with a high unit mass of the specific strength and stiffness, not easy to deformation, completely overcoming the collapse and deformation in the center area if with large panel. The panel edge can be cut depending on real conditions. The PVDF coating can guarantee the product life more than 30 years.
After surface treated with corrosion resistant fluorocarbon resin, it can be widely used on curtain wall, roof, large façade, signs and interior decoration. The front plate of the aluminum honeycomb panel is painted with E. C. C. A. quality standards PVDF fluorocarbon paint with ordinary color or metallic color, so the surface has excellent weather resistance.
In case of heavy rain, there is particularly large noise when the raindrops hit the aluminum veneer or aluminum-plastic panel, while honeycomb panel can avoid this situation. Aluminum honeycomb panels are generally made of fluorocarbon coated aluminum plates. The continuous roller coating with PVDF material is the most important point to avoid color difference and flat coating film. Based on this, it can keep the exterior building with bright color for long time.
|Unit theory weight||kg/m2||5.4||5.6||5.75|
|Bend elasticity rate||N/mm2||50000||40600||38.44|
|Temeprature total extension coefficient||D696||X10-6N/℃||0.24||0.24||0.24|
|Heat conduction rate||D976||Kcal/mhr℃||0.23||0.19||0.15|
|Heat transform temperature||D648||℃||200||200||200|
|Surtace smoothness||1mm/M.Maximum deviation:1mm/M|
|Flame retardabt property||Nonflammable,match relevant fire resistance standard|
|Soundproof function||Be decided by layout of printed sheet installation angle,0-3dB|